| 1771 - 450 Seiten
...necessary, before immersing them, to permit the triple alloy to dissolve or combine with some wrought iron, in order that its affinity for iron may be partially...fusing temperature of this alloy, which is about 680" of Fahrenheit's thermometer, it will dissolve a plate of wrought iron, of an eighth of an inch thick,... | |
| 1842 - 548 Seiten
...necessary before immersing them to permit the triple alloy to dissolve or combine with some wrought iron, in order that its affinity for iron may be partially...which is about 680° Fahr. it will dissolve a plate of wrought iron of an eighth of an inch thick in a few seconds. No sputtering is produced by the immersion... | |
| Perry Fairfax Nursey - 1842 - 538 Seiten
...necessary before immersing them to permit the triple alloy to dissolve or combine with some wrought iron, in order that its affinity for iron may be partially...proper fusing temperature of this alloy, which is about (№0° Fahr, it will dissolve a plate of wrought iron of an eighth of an inch thick in a few seconds.... | |
| 1842 - 934 Seiten
...necessary before immersing them, to permit the triple alloy to< dissolve or combine with some wrought iron, in order that its affinity for iron may be partially...the proper fusing temperature of this alloy, which isabout 680° Fahr. it will dissolve a plate of wrought iron of an eighth of an inch thick in a few... | |
| 1842 - 886 Seiten
...necessary before immersing them to permit the triple alloy to dissolve or combine with some wrought iron, in order that its affinity for iron may be partially...diminished. At the proper fusing temperature of this alloy, whicii is about 680° Fahr. it will dissolve a plate of wrought iron of an eighth of an inch thick... | |
| Charles Holtzapffel - 1843 - 496 Seiten
...dissolved. Indeed where the articles to be covered are small, or their parts minute, such as wire or nails or small chain, it is necessary before immersing...inch thick in a few seconds." " The palladiumizing process.—The articles to be protected are to be first cleansed in the same way as in the case of... | |
| British Association for the Advancement of Science - 1844 - 480 Seiten
...necessary, before immersing them, to permit the alloy to dissolve or combine with some wrought iron, in order that its affinity for iron may be partially satisfied, and so this risk be avoided. The alloy will, at its proper fusing temperature, which is about 680° Fahr.,... | |
| 1847 - 906 Seiten
...necessary, before immersing them, to permit the alloy to dissolve or combine with some wrought iron, in order that its affinity for iron may be partially satisfied, and so this risk be avoided. The alloy will, at its proper fusing temperature, which is about 680° Fahr.,... | |
| Cyclopaedia - 1852 - 258 Seiten
...artieles to be covered are small, or the parts minute, as for example, wire, nails, or small chains, it is necessary before immersing them to permit the...iron may be partially satisfied, and thus diminished. In the palladinmizing process the artieles to be protected are first eleansed as in zincing, and then... | |
| Cyclopaedia - 1852 - 268 Seiten
...small ehains, it is neeessary before immersing them to permit the triple alloy to dissolve, or eombine with some wrought-iron, in order that its affinity...iron may be partially satisfied, and thus diminished. In the palladinmizing proeess the artieles to be proteeted are first eleansed as in zineing, and then... | |
| |